SS410 | X12Cr13 | 410
.jpg)
Key Features
-
Good Corrosion Resistance
-
Magnetic in All Conditions
-
Excellent Machinability in Annealed State
-
Versatile Heat Treatment Response
Size Range
Round Bar
80 mm To 500 mm Diameter
Flat Bar
80mm*80mm To 510mm*360mm
About the Steel
SS410 stainless steel is a martensitic stainless steel that offers a balance of strength, hardness, and moderate corrosion resistance. It can be easily machined in the annealed condition and develops high hardness and wear resistance after heat treatment. SS410 performs well in mildly corrosive environments, but it is less resistant to corrosion compared to austenitic stainless steels. Its toughness decreases at higher hardness levels, making it best suited for moderate wear and low-impact applications where both strength and corrosion resistance are required.
Applications
-
Pump & Valve Components
Ideal for shafts, spindles, and seats exposed to water and mild chemicals.
-
Petrochemical & Power Equipment
Applied in parts needing wear resistance and moderate corrosion protection.
-
Automotive & Aerospace Components
Used for structural parts that require strength and heat resistance.
-
General Engineering Parts
Shafts, bushings, and gears where hardness and moderate corrosion resistance are needed.
-
Industrial Fasteners & Bolts
Suitable for moderate-strength corrosion-resistant hardware.
Manufacturing
Process flow for manufacturing 410 steel
Melting
Ingots melted in EIF, impurities fully killed and followed LRF and VD process at Client's request. Ingots annealed
Forging
Press or Hammer Forged with reduction ratio of 3.5 to 4.5 times
Heat Treatment
Full annealing cycle post forging or any special QT process as per Client's TDC
Quality Test
Ultrasonic, Hardness, Mechanical, Microstructure testing of the metal at a NABL approved lab
Proof Machining
Proof machining of Forged Rounds and Flats as per Client's requirements